Electrically conductive PEEK composite having CNT (carbon nano-tube) fillers. The surface resistance is 102 - 104 Ohm. Developed for electronics and electrical industry.
Product properties
Color:
black
Electrically insulator:
No
main area of use:
Non-insulating applications (anti-static, ESD), Raised temperature applications, Excellent chemical resistance
Printable materials
Properties | Unit | Method | Value |
---|---|---|---|
Colour | |||
Density | g/cm3 | DIN EN ISO 1183 | 1.36 |
Flammability (UL94) | - | DIN IEC 60695-11-10 | V0 |
Water absorption in air, 24 h / 96 h, (23ºC) | % | DIN EN ISO 62 | 0.02/ 0.03 |
Dielectric constant | - | IEC 60250 | |
Volume resistivity | Ω*cm | IEC60093 | 105 |
Surface resistivity | Ω | IEC60093 | 104 |
Dielectric strength | kV/mm | IEC 60243 | |
Dielectric dissipation factor (50 Hz) | - | IEC60 250 | |
Comparative tracking index (CTI) | - | IEC 60112 | |
Thermal conductivity | W/ (K.m) | ISO 22007-4:2008 | 0.46 |
Chemical resistance at 23ºC: deluted acids | - | A* | |
Chemical resistance at 23ºC: strong acids | - | A-B* | |
Chemical resistance at 23ºC: aliphatic hydrocarbons | - | A* | |
Chemical resistance at 23ºC: chlorin dissolvents | - | A* | |
Chemical resistance at 23ºC: alcohols | A* | ||
Chemical resistance at 23ºC: deluted bases | - | A* | |
Chemical resistance at 23ºC: strong bases | - | A* | |
Chemical resistance at 23ºC: aromatic hydrocarbons | - | A* | |
Melting temperature | ºC | ISO 11357-3 | 341 |
Glass transition temperature | ºC | DIN 53765 | 147 |
Specific heat | J/(g.K) | ISO 22007-4:2008 | 1.1 |
Coefficient of linear thermal expansion (CLTE): 23 - 60ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 5 |
Coefficient of linear thermal expansion (CLTE): 23 - 100ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 5 |
Max. allowable service temperature in air, short term | ºC | 300 | |
Max. allowable service temperature in air, long term | ºC | 260 | |
Min. allowable service temperature in air, long term | ºC | - 40 | |
Heat deflection temperature | ºC | DIN EN ISO 75, A | |
Yield stress | MPa | DIN EN ISO 527-2 | 106 |
Modulus of elasticity (tensile test) | MPa | DIN EN ISO 527-2 | 4800 |
Elongation at break | % | DIN EN ISO 527-2 | 4 |
Flexural strength | MPa | DIN EN ISO 178 | 178 |
Impact strength, Charpy | kJ/m2 | DIN EN ISO 179-1eU | 58 |
Tensile strength | MPa | DIN EN ISO 527-2 | 106 |
Compressive strength | MPa | EN ISO 604 1% / 2% | 27 / 47 |
Notched impact strength, charpy | kJ/m2 | DIN EN ISO 179-1eA | |
Ball indentation hardness | MPa | ISO 2039-1 | 253 |
Shore D hardness | - | DIN EN ISO 868 | 88 |
(*) legend:
- A – applicable
- B – partially applicable
- C – not applicable
Rods
Filter by colors
There are no products for the given parameters, please choose another size / color.
Plates
Filter by colors
There are no products for the given parameters, please choose another size / color.