Natural colored, unfilled polyamide 12. In comparison with the polyamide 6 materials, it has a smaller degree of water absorption, the material is extremely tough, resistant to cyclic fatigue stress and it has good abrasion wear resistance.
Product properties
Color:
natural
Electrically insulator:
Yes
main area of use:
Basic stucture material
Printable materials
| Properties | Unit | Method | Value |
|---|---|---|---|
| Colour | |||
| Density | g/cm3 | DIN EN ISO 1183 | 1.02 |
| Flammability (UL94) | - | DIN IEC 60695-11-10 | HB |
| Water absorption in air, 24 h / 96 h, (23ºC) | % | DIN EN ISO 62 | 0.04/ 0.07 |
| Dielectric constant | - | IEC 60250 | 3.8 |
| Volume resistivity | Ω*cm | IEC60093 | 1014 |
| Surface resistivity | Ω | IEC60093 | 1014 |
| Dielectric strength | kV/mm | IEC 60243 | 26 |
| Dielectric dissipation factor (50 Hz) | - | IEC60 250 | 0.04 |
| Comparative tracking index (CTI) | - | IEC 60112 | 600 |
| Thermal conductivity | W/ (K.m) | ISO 22007-4:2008 | 0.3 |
| Chemical resistance at 23ºC: deluted acids | - | B* | |
| Chemical resistance at 23ºC: strong acids | - | C* | |
| Chemical resistance at 23ºC: aliphatic hydrocarbons | - | A* | |
| Chemical resistance at 23ºC: chlorin dissolvents | - | B* | |
| Chemical resistance at 23ºC: alcohols | A* | ||
| Chemical resistance at 23ºC: deluted bases | - | A* | |
| Chemical resistance at 23ºC: strong bases | - | B - C* | |
| Chemical resistance at 23ºC: aromatic hydrocarbons | - | A* | |
| Melting temperature | ºC | ISO 11357-3 | 178 |
| Glass transition temperature | ºC | DIN 53765 | 37 |
| Specific heat | J/(g.K) | ISO 22007-4:2008 | 1.8 |
| Coefficient of linear thermal expansion (CLTE): 23 - 60ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 15 |
| Coefficient of linear thermal expansion (CLTE): 23 - 100ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 16 |
| Max. allowable service temperature in air, short term | ºC | 150 | |
| Max. allowable service temperature in air, long term | ºC | 100 | |
| Min. allowable service temperature in air, long term | ºC | - 50 | |
| Heat deflection temperature | ºC | DIN EN ISO 75, A | 50 |
| Yield stress | MPa | DIN EN ISO 527-2 | 53 |
| Modulus of elasticity (tensile test) | MPa | DIN EN ISO 527-2 | 1800 |
| Elongation at break | % | DIN EN ISO 527-2 | 200 |
| Flexural strength | MPa | DIN EN ISO 178 | 68 |
| Impact strength, Charpy | kJ/m2 | DIN EN ISO 179-1eU | nem törik |
| Tensile strength | MPa | DIN EN ISO 527-2 | 53 |
| Compressive strength | MPa | EN ISO 604 1% / 2% | 13 / 24 |
| Notched impact strength, charpy | kJ/m2 | DIN EN ISO 179-1eA | 7 |
| Ball indentation hardness | MPa | ISO 2039-1 | 105 |
| Shore D hardness | - | DIN EN ISO 868 | 78 |
(*) legend:
- A – applicable
- B – partially applicable
- C – not applicable
Rods
Filter by colors
There are no products for the given parameters, please choose another size / color.
Plates
Filter by colors
There are no products for the given parameters, please choose another size / color.