Especially produced for implant application in medical activity.
Product properties
Color:
white
Electrically insulator:
Yes
main area of use:
Medical applications, Exceptional gliding and wear-proof properties
Printable materials
| Properties | Unit | Method | Value |
|---|---|---|---|
| Colour | |||
| Density | g/cm3 | DIN EN ISO 1183 | 0.93 |
| Flammability (UL94) | - | DIN IEC 60695-11-10 | HB |
| Water absorption in air, 24 h / 96 h, (23ºC) | % | DIN EN ISO 62 | <0.01 |
| Dielectric constant | - | IEC 60250 | 2.3 |
| Volume resistivity | Ω*cm | IEC60093 | >1014 |
| Surface resistivity | Ω | IEC60093 | >1014 |
| Dielectric strength | kV/mm | IEC 60243 | 45 |
| Dielectric dissipation factor (50 Hz) | - | IEC60 250 | 0.0001 |
| Comparative tracking index (CTI) | - | IEC 60112 | 600 |
| Thermal conductivity | W/ (K.m) | ISO 22007-4:2008 | 0.4 |
| Chemical resistance at 23ºC: deluted acids | - | A* | |
| Chemical resistance at 23ºC: strong acids | - | A* | |
| Chemical resistance at 23ºC: aliphatic hydrocarbons | - | B* | |
| Chemical resistance at 23ºC: chlorin dissolvents | - | B* | |
| Chemical resistance at 23ºC: alcohols | A* | ||
| Chemical resistance at 23ºC: deluted bases | - | A* | |
| Chemical resistance at 23ºC: strong bases | - | A* | |
| Chemical resistance at 23ºC: aromatic hydrocarbons | - | B* | |
| Melting temperature | ºC | ISO 11357-3 | 135 |
| Glass transition temperature | ºC | DIN 53765 | |
| Specific heat | J/(g.K) | ISO 22007-4:2008 | 1,9 |
| Coefficient of linear thermal expansion (CLTE): 23 - 60ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 150 |
| Coefficient of linear thermal expansion (CLTE): 23 - 100ºC | m/(m.K)x10-5 | DIN EN ISO 11359-1;2 | 230 |
| Max. allowable service temperature in air, short term | ºC | 130 | |
| Max. allowable service temperature in air, long term | ºC | 80 | |
| Min. allowable service temperature in air, long term | ºC | - 250 | |
| Heat deflection temperature | ºC | DIN EN ISO 75, A | 79 |
| Yield stress | MPa | DIN EN ISO 527-2 | 20 |
| Modulus of elasticity (tensile test) | MPa | DIN EN ISO 527-2 | 680 |
| Elongation at break | % | DIN EN ISO 527-2 | >200 |
| Flexural strength | MPa | DIN EN ISO 178 | |
| Impact strength, Charpy | kJ/m2 | DIN EN ISO 179-1eU | |
| Tensile strength | MPa | DIN EN ISO 527-2 | |
| Compressive strength | MPa | EN ISO 604 1% / 2% | |
| Notched impact strength, charpy | kJ/m2 | DIN EN ISO 179-1eA | nem törik |
| Ball indentation hardness | MPa | ISO 2039-1 | |
| Shore D hardness | - | DIN EN ISO 868 | 63 |